Strontium - 4GB MicroSD [ Deep Body Scratch Recovery ]

[Amarbir[CDR-Labs]]

Hello ,
I Have got this case from a client .To me it seems somehow the client has damaged it with a deep " Not so deep " scratch .This is a 4GB Strontium Micro SD .I have Tried Finding a Similiar Micro SD Online so that i could try and reconstruct the same .But i have not managed to do that .Not Only This i Have Not Managed To See This Kinda Micro SD At Acelab Solbase Also In The Monolith Chips .I Do Have PC 3000 Flash " But Its Older Version 1.0 " . Has Someone Come Across Such a Micro SD Card And Can I Have Some Suggestions .Photo Are Added

The Top Side Of The MicroSD Card



The Bottom Side Of The Micro SD Card





Damaged Section Of The Card







PS : It Seems To Me Approx 5 Tracks Are Damaged

[HaQue]

I have a MicroSD with similar issue, 2 tracks worn thru from inserting and removing. the tracks seemed easily fixed, but still did not work after a pretty good looking repair.

I don't have pinout either

[Amarbir[CDR-Labs]]

I have a MicroSD with similar issue, 2 tracks worn thru from inserting and removing. the tracks seemed easily fixed, but still did not work after a pretty good looking repair.

I don't have pinout either

Sir ,
I Do Not Need Pinouts ,I Just Need a Image Of The Same Without Any Damage So That i Can Reconstruct The Tracks HaQue .

[HaQue]

I have looked at all the monolith databases I know and seen none the same.

I have a bad feeling there are 3 VIAs that have been scraped off at the end of the traces. an X-Ray would be useful if you cant get a match. you can probably get one done at a reasonable cost somewhere

[Amarbir[CDR-Labs]]

I have looked at all the monolith databases I know and seen none the same.

I have a bad feeling there are 3 VIAs that have been scraped off at the end of the traces. an X-Ray would be useful if you cant get a match. you can probably get one done at a reasonable cost somewhere

Well,
You Want Me To Get a Xray Of This Chip .Might Be a Dental Grade Xray With a Small Film Would Be Ok .Before i Do That Might Be Someone Else Can Comment On This Subject